高级搜索

锰氧化物八面体分子筛活化过一硫酸氢盐降解酸性橙7

,  ,  , 

downloadPDF

上一篇

下一篇

熊易玄, 柯雪珍, 陈成, 徐爱华. 锰氧化物八面体分子筛活化过一硫酸氢盐降解酸性橙7[J]. 环境工程学报, 2016, 10(10): 5600-5604. doi: 10.12030/j.cjee.201504203
引用本文: 熊易玄, 柯雪珍, 陈成, 徐爱华. 锰氧化物八面体分子筛活化过一硫酸氢盐降解酸性橙7[J]. 环境工程学报, 2016, 10(10): 5600-5604. doi: 10.12030/j.cjee.201504203
shu
XIONG Yixuan, KE Xuezhen, CHEN Cheng, XU Aihua. Heterogeneous activation of peroxymonosulfate by cryptomelane type manganese oxide for Acid Orange 7 degradation in aqueous solutions[J]. Chinese Journal of Environmental Engineering, 2016, 10(10): 5600-5604. doi: 10.12030/j.cjee.201504203
Citation: XIONG Yixuan, KE Xuezhen, CHEN Cheng, XU Aihua. Heterogeneous activation of peroxymonosulfate by cryptomelane type manganese oxide for Acid Orange 7 degradation in aqueous solutions[J]. Chinese Journal of Environmental Engineering, 2016, 10(10): 5600-5604. doi: 10.12030/j.cjee.201504203
shu

锰氧化物八面体分子筛活化过一硫酸氢盐降解酸性橙7

  • 1.

    武汉纺织大学环境工程学院, 武汉 430200

  • 基金项目:

    国家自然科学基金资助项目（21207015）

  • 中图分类号: X703.1

Heterogeneous activation of peroxymonosulfate by cryptomelane type manganese oxide for Acid Orange 7 degradation in aqueous solutions

  • 1.

    School of Environmental Engineering, Wuhan Textile University, Wuhan 430200, China

  • Fund Project:

  • 摘要: 采用无溶剂法制备了氧化锰八面体分子筛（OMS-2），通过XRD、FT-IR、SEM、TEM及N2吸附-脱附等温线等对其结构进行了表征，并以典型难降解偶氮染料酸性橙7（AO7）为目标污染物，考察了OMS-2活化过一硫酸氢盐（PMS）降解AO7的性能。研究结果发现，无溶剂法制备的OMS-2呈纳米棒状，为典型的锰钾矿型结构，比表面积达到129 m2·g-1，平均粒径10.5 nm左右。OMS-2催化剂能够高效催化PMS产生活性自由基降解偶氮染料，反应10 min内可使AO7几乎完全脱色，重复使用10次均能保持较高的催化稳定性；脱色降解后染料分子中的共轭体系和芳香环结构被破坏。
    Abstract: Cryptomelane-type manganese oxide, OMS-2, was prepared by a solvent-free process, and characterized by X-ray diffraction, scanning electron microscopy, N2 adsorption/desorption isotherms, and fourier transform infrared spectroscopy. The activity and stability of the catalyst were tested for degradation of Acid Orange 7 (AO7) in the presence of peroxymonosulfate. OMS-2 exhibited the typical cryptomelane phase with a nanorod morphology, and had a surface area of 129 m2·g-1 and crystallite size of 11 nm. The catalyst was quite active for AO7 degradation, with production of sulfate radicals;AO7 was completely decolorized within 10 min due to the destruction of its conjugate structure and naphthaquinone ring. The catalyst also exhibited a high stability over ten cycles.
  • 加载中
  • [1] 张宇峰, 滕洁, 张雪英, 等. 印染废水处理技术的研究进展. 工业水处理,2003, 23(4): 23-27 ZHANG Yufeng, TENG Jie, ZHANG Xueying, et al. Progress of the researches on dyeing wastewater treatment techniques. Industrial Water Treatment, 2003, 23(4): 23-27(in Chinese)
    [2] 钟恒, 曹文彪, 熊重铎, 等. 铈离子光催化降解茜素绿的性能和机理. 环境工程学报, 2014,8(2): 448-452 ZHNG Heng, CAO Wenbian, XIONG Zhongduo, et al. Activity and mechanism of photocatalytic degradaion of Alizan Green by cerium ions. Chinese Journal of Environmental Engineering, 2014,8(2): 448-452(in Chinese)
    [3] LUO M., LYU L., DENG G., et al. The mechanism of bound hydroxyl radical formation and degradation pathway of Acid Orange II in Fenton-like Co2+-HCO3- system. Applied Catalysis A: Genera, 2014, 469: 198-205
    [4] KHAN J. A., HE X, KHAN H. M., et al. Oxidative degradation of atrazine in aqueous solution by UV/H2O2/Fe2+, UV/S2O82-/Fe2+ and UV/HSO5-/Fe2+ processes: A comparative study. Chemical Engineering Journal, 2013, 218: 376-383
    [5] NFODZO P., CHOI H. Triclosan decomposition by sulfate radicals: Effects of oxidant and metal doses. Chemical Engineering Journal, 2011, 174(2/3): 629-634
    [6] ZHANG J., SHAO X., SHI C., et al. Decolorization of Acid Orange 7 with peroxymonosulfate oxidation catalyzed by granular activated carbon. Chemical Engineering Journal, 2013, 232: 259-265
    [7] CHEN X., CHEN J., QIAO X., et al. Performance of nano-Co3O4/peroxymonosulfate system: Kinetics and mechanism study using Acid Orange 7 as a model compound. Applied Catalysis B:Environmental, 2008, 80(1/2): 116-121
    [8] SHI P., SU R., ZHU S., et al. Supported cobalt oxide on graphene oxide: Highly efficient catalysts for the removal of Orange II from water. Journal of Hazardous Materials, 2012, 229: 331-339
    [9] JI F., LI C., WE Xi. Efficient performance of porous Fe2O3 in heterogeneous activation of peroxymonosulfate for decolorization of Rhodamine B. Chemical Engineering Journal, 2013, 231: 434-440
    [10] LIU J., ZHAO Z., SHAO P., et al. Activation of peroxymonosulfate with magnetic Fe3O4-MnO2 core-shell nanocomposites for 4-chlorophenol degradation. Chemical Engineering Journal, 2015, 262: 854-861
    [11] ZHANG T., ZHU H., CROU J. P. Production of sulfate radical from peroxymonosulfate induced by a magnetically separable CuFe2O4 spinel in water: Efficiency, stability, and mechanism. Environmental Science & Technology, 2013,47(6): 2784-2791
    [12] SAPUTRA E., MUHAMMAD S., SUN H., et al. Manganese oxides at different oxidation states for heterogeneous activation of peroxymonosulfate for phenol degradation in aqueous solutions. Applied Catalysis B:Environmental, 2013, 142-143: 729-735
    [13] CHEN X., SHEN Y., SUIB S. L., et al. Catalytic decomposition of 2-propanol over different metal-cation-doped OMS-2 materials. Journal of Catalysis, 2001, 197(2): 292-302
    [14] KUMAR R., SITHAMBARAM S., SUIB S. L. Cyclohexane oxidation catalyzed by manganese oxide octahedral molecular sieves: Effect of acidity of the catalyst. Journal of Catalysis, 2009, 262(2): 304-313
    [15] YANG Y., HUANG J., ZHANG S., et al. Catalytic removal of gaseous HCBz on Cu doped OMS: Effect of Cu location on catalytic performance. Applied Catalysis B: Environmental, 2014, 150: 167-178
    [16] 刘雪松,鲁继青,王晓霞,等.OMS-2的制备及其负载PdO对CO氧化的催化活性. 催化学报, 2010, 3(2): 181-185 LIU Xuesong, LU Jiqing, WANG Xiaoxia, et al. Preparation of manganese oxide octahedral molecular sieve and catalytic activity of its supported PdO for CO oxidation. Chinese Journal of Catalysis, 2010, 3(2): 181-185(in Chinese)
    [17] LUO S., DUAN L., SUN B., et al. Manganese oxide octahedral molecular sieve (OMS-2) as an effective catalyst for degradation of organic dyes in aqueous solutions in the presence of peroxymonosulfate. Applied Catalysis B:Environmental, 2015, 164: 92-99
    [18] DUAN L., SUN B., WEI M., et al. Catalytic degradation of Acid Orange 7 by manganese oxide octahedral molecular sieves with peroxymonosulfate under visible light irradiation. Journal of Hazardous Materials, 2015, 285: 356-365
    [19] 王燕彩, 刘昕, 宁平, 等. 制备方法对氧化锰八面体分子筛的NH3选择性催化还原NOx性能的影响. 燃料化学学报, 2014, 42(11): 1357-136 WANG Yancai, LIU Xin, NING Ping, et al. Effect of preparation methods on selective catalytic reduction of NOx with NH3 over manganese oxide octahedral molecular sieves. Journal of Fuel Chemistry and Technology, 2014, 42(11): 1357-136
    [20] DING Y., SHEN X., SITHAMBARAM S., et al. Synthesis and catalytic activity of cryptomelane-type manganese dioxide nanomaterials produced by a novel solvent-free method. Chemistry of Materials, 2006, 17(21): 5382-5389
    [21] 余林, 孙明, 余坚, 等. 锰八面体分子筛的合成、表征及其对二甲醚燃烧的催化性能. 催化学报, 2008, 29(11): 1127-1132 YU Lin, SUN Ming, YU Jian, et al. Synthesis and characterization of manganese oxide octahedral molecular sieve catalyt for DME combustion. Chinese Journal of Catalysis, 2008, 29(11): 1127-1132(in Chinese)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  1409
  • HTML全文浏览数:  1039
  • PDF下载数:  461
  • 施引文献:  0
出版历程
  • 收稿日期:  2015-06-18
  • 刊出日期:  2016-10-20

锰氧化物八面体分子筛活化过一硫酸氢盐降解酸性橙7

  • 1. 武汉纺织大学环境工程学院, 武汉 430200
  • 收稿日期:  2015-06-18
基金项目:

国家自然科学基金资助项目（21207015）

摘要: 采用无溶剂法制备了氧化锰八面体分子筛（OMS-2），通过XRD、FT-IR、SEM、TEM及N2吸附-脱附等温线等对其结构进行了表征，并以典型难降解偶氮染料酸性橙7（AO7）为目标污染物，考察了OMS-2活化过一硫酸氢盐（PMS）降解AO7的性能。研究结果发现，无溶剂法制备的OMS-2呈纳米棒状，为典型的锰钾矿型结构，比表面积达到129 m2·g-1，平均粒径10.5 nm左右。OMS-2催化剂能够高效催化PMS产生活性自由基降解偶氮染料，反应10 min内可使AO7几乎完全脱色，重复使用10次均能保持较高的催化稳定性；脱色降解后染料分子中的共轭体系和芳香环结构被破坏。