含钒钢渣低温钠化焙烧钒浸出效果及其焙砂湿法脱硫作用

,  ,  , 

downloadPDF

上一篇

下一篇

王洁, 刘树根, 宁平, 谢容生. 含钒钢渣低温钠化焙烧钒浸出效果及其焙砂湿法脱硫作用[J]. 环境工程学报, 2018, 12(11): 3124-3130. doi: 10.12030/j.cjee.201804071
引用本文: 王洁, 刘树根, 宁平, 谢容生. 含钒钢渣低温钠化焙烧钒浸出效果及其焙砂湿法脱硫作用[J]. 环境工程学报, 2018, 12(11): 3124-3130. doi: 10.12030/j.cjee.201804071
shu
WANG Jie, LIU Shugen, NING Ping, XIE Rongsheng. Sodium salt roasting of vanadium-containing steel slag at low temperature and application of vanadium calcine for wet desulfurization[J]. Chinese Journal of Environmental Engineering, 2018, 12(11): 3124-3130. doi: 10.12030/j.cjee.201804071
Citation: WANG Jie, LIU Shugen, NING Ping, XIE Rongsheng. Sodium salt roasting of vanadium-containing steel slag at low temperature and application of vanadium calcine for wet desulfurization[J]. Chinese Journal of Environmental Engineering, 2018, 12(11): 3124-3130. doi: 10.12030/j.cjee.201804071
shu

含钒钢渣低温钠化焙烧钒浸出效果及其焙砂湿法脱硫作用

  • 1.

    昆明理工大学环境科学与工程学院，昆明 650500

  • 2.

    共伴生有色金属资源加压湿法冶金技术国家重点实验室，昆明 650503

  • 基金项目:

    共伴生有色金属资源加压湿法冶金技术国家重点实验室开放基金资助项目（yy2016004）

    昆明理工大学分析测试基金资助项目（2017M20162207026）

Sodium salt roasting of vanadium-containing steel slag at low temperature and application of vanadium calcine for wet desulfurization

  • 1.

    Faculty of Environmental Science and Engineering, Kunming University of Science and Technology, Kunming 650500, China

  • 2.

    State Key Laboratory of Pressure Hydrometallurgical Technology of Associated Nonferrous Metal Resources, Kunming 650503, China

  • Fund Project:

  • 摘要: 含钒钢渣钠化焙烧过程中添加CaF2等助剂以降低提钒工艺的能耗，分析了不同因素对低温钠化焙烧后钒浸出效果的影响，并将含钒钢渣焙砂配制成吸收浆液以净化烟气中的SO2。在浸出钒实现其资源化利用的同时，也探索出一种高效烟气脱硫的新方法。添加3.0% CaF2作为助剂，温度为700 ℃、焙烧时间为1 h的条件下，所得焙砂中钒浸出率可达68.1%。X射线衍射（XRD）与热重（TG）分析表明，混合物料中添加CaF2助剂能促进焙烧过程物相的改变，白云母、钛铁矿等衍射峰明显减弱，含钒钢渣混合料在700 ℃条件下便呈现明显的热失重，在较低温度条件下即可实现钠化焙烧。以此含钒焙砂配制脱硫吸收浆液，脱硫率不低于95%的穿透时间可达125 min，而同样条件下磷矿浆脱硫系统仅为35 min。
    Abstract: In this study, CaF2 or other additives were added to the mixture containing vanadium steel slag for energy consumption reduction during vanadium extraction process. The effects of technical parameters on vanadium leaching, as well as the vanadium calcine used as absorption slurry to purify sulfur dioxide in flue gas, were investigated. The results show that vanadium recovery could be successfully achieved, and an innovative approach for efficient flue gas desulfurization was also found. At CaF2 addition ratio of 3.0%, the roasting temperature of 700 ℃ and retention time of 1 h, the leaching rate of vanadium could reach 68.1%. Based on the analysis of X-ray diffraction (XRD) and thermogravimetry (TG), the additive CaF2 was in favor of the mineral phase change during roasting process, which led to the significant weakening on the diffraction peaks of muscovite and ilmenite. Thus, a remarkable heat loss occurred for the mixing system at the TG temperature of 700 ℃, then sodium salt roasting of vanadium-containing steel slag could be achieved at a relatively low temperature. The vanadium calcine was used as a kind of wet desulfurization agent, and the breakthrough time reached 125 minutes as desulfurization efficiency was not less than 95%, however, it was only 35 minutes for the desulfurization system with phosphate ore slurry.
  • 加载中
  • [1] 张冬冬，魏爱斌，张晋鸣，等．液相催化氧化SO2研究进展 [J]．昆明理工大学学报(自然科学版),2015,40(5):97-107
    [2] 刘娜，孙鑫，宁平，等．新型矿浆材料脱硫现状及研究进展 [J]．材料导报,2017,31(17):106-111
    [3] JIANG W J．Simultaneous absorption of NOx and SO2 from flue gas with pyrolusite slurry combined with gas-phase oxidation of NO using ozone[J]．Journal of Hazardous Materials,2011,192(1):124-130 10.1016/j.jhazmat.2011.04.104
    [4] 刘卉卉，宁平．磷矿浆催化氧化湿法脱硫研究(Ⅱ) [J]．化工矿物与加工,2005,34(7):10-12
    [5] 周晓龙．半钢钢渣脱除烟气中二氧化硫的实验研究 [D]．北京: 北京建筑大学,2015
    [6] 刘盛余，邱伟，汪雪婷．柠檬酸强化钢渣湿法烧结烟气脱硫及机理 [J]．环境工程学报,2015,9(3):1323-1328
    [7] 邱伟，刘盛余，能子礼超．氢氧化钠-钢渣双碱法烧结烟气脱硫工艺 [J]．环境工程学报,2013,7(3):1095-1100
    [8] 付自碧．钒渣钙化焙烧-酸浸提钒试验研究 [J]．钢铁钒钛,2014,35(1):1-6
    [9] 叶露．钒渣钙化焙烧熟料酸浸过程钒溶解规律研究 [J]．钢铁钒钛,2017,38(5):20-25
    [10] 何文艺．钒渣钙化熟料硫酸浸出试验研究 [J]．中国锰业,2017,35(3):112-117
    [11] 王春琼．钙化焙烧含钒熟料硫酸浸出工艺研究 [J]．钢铁钒钛,2016,37(1):26-30
    [12] 杨冲．石煤提钒钠化焙烧工艺尾气产生的影响因素及机理研究 [D]．南昌:南昌大学,2011
    [13] NAVARRO R，GUZMAN J，SAUCEDO I，et al．Vanadium recovery from oil fly ash by leaching，precipitation and solvent extraction processes[J]．Waste Management,2007,27(3):425-438 10.1016/j.wasman.2006.02.002
    [14] MAZUREK K．Recovery of vanadium potassium and iron from a spent vanadium catalyst by oxalic acid solution leaching precipitation and ion exchange processes[J]．Hydrometallurgy,2013,134-135(3):26-31 10.1016/j.hydromet.2013.01.011
    [15] 李兰杰，张力，郑诗礼，等．钒钛磁铁矿钙化焙烧及其酸浸提钒 [J]．过程工程学报,2011,11(4):573-578
    [16] 蔡永红，赵昌明，宁哲，等．熔融Na2CO3体系中含钒钢渣焙烧过程研究 [J]．矿冶工程,2017(6):76-79
    [17] 华一新．冶金过程动力学导论 [M]．北京: 冶金工业出版社,2004
    [18] 陶雷，王学谦，宁平，等．矿浆烟气脱硫及资源化研究进展 [J]．化工进展,2017,36(5):1868-1879
    [19] 付朝阳，张一敏，刘涛，等．一步法石煤提钒反萃液酸性铵盐沉钒试验研究 [J]．稀有金属,2015(5):462-467
    [20] BRANT C，ELDIK R．Transition metal-catalyzed oxidation of sulfur (Ⅳ) oxides．Atmospheric-relevant processes and mechanisms[J]．Chemical Reviews,1995,95(1):119-190 10.1021/cr00033a006
    [21] PASIUK B W，BRONIKOWSKI T．The rate equation for SO2 autoxidation in aqueous MnSO4 solution containing H2SO4[J]．Chemical Engineering Science,1981,36(2):215-219 10.1016/0009-2509(81)80069-3
    [22] HUSS J A，LIM P K．Oxidation of aqueous SO2 homogenese manganese(Ⅱ) and iron(Ⅱ) catalysts at low pH[J]．Journal of Chemical Physics,1982,86(21):4224-4228 10.1021/j100218a027
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  3517
  • HTML全文浏览数:  3407
  • PDF下载数:  152
  • 施引文献:  0
出版历程
  • 刊出日期:  2018-11-12

含钒钢渣低温钠化焙烧钒浸出效果及其焙砂湿法脱硫作用

  • 1. 昆明理工大学环境科学与工程学院，昆明 650500
  • 2. 共伴生有色金属资源加压湿法冶金技术国家重点实验室，昆明 650503
基金项目:

共伴生有色金属资源加压湿法冶金技术国家重点实验室开放基金资助项目（yy2016004）

昆明理工大学分析测试基金资助项目（2017M20162207026）

摘要: 含钒钢渣钠化焙烧过程中添加CaF2等助剂以降低提钒工艺的能耗，分析了不同因素对低温钠化焙烧后钒浸出效果的影响，并将含钒钢渣焙砂配制成吸收浆液以净化烟气中的SO2。在浸出钒实现其资源化利用的同时，也探索出一种高效烟气脱硫的新方法。添加3.0% CaF2作为助剂，温度为700 ℃、焙烧时间为1 h的条件下，所得焙砂中钒浸出率可达68.1%。X射线衍射（XRD）与热重（TG）分析表明，混合物料中添加CaF2助剂能促进焙烧过程物相的改变，白云母、钛铁矿等衍射峰明显减弱，含钒钢渣混合料在700 ℃条件下便呈现明显的热失重，在较低温度条件下即可实现钠化焙烧。以此含钒焙砂配制脱硫吸收浆液，脱硫率不低于95%的穿透时间可达125 min，而同样条件下磷矿浆脱硫系统仅为35 min。